UNIASLON TB grade

Linear-cut nylon film

This is special nylon film developed by a combination of bi-axially orientation technology under Idemitsu's original precision orientation control system and material reformation technology. Allowing full utilization of the properties common to nylon resins maintains practical strength as well as linear cutting properties. This product is also applicable for a wide range of applications from frozen food to thermal and retort food thanks to its excellent suitability for printing and laminating.

Grade List

Category Linear-cut nylon film Test method
Grade name UNIASLON TB-1000 UNIASLON TB-1010
Application General-purpose packing Thermal and retort General-purpose packing Thermal and retort
Characteristics Linear-cut properties (MD direction) Gas barrier property Linear-cut properties (MD direction) Gas barrier property Double-side corona processing
Thickness (µm) 15 15 -
Tensile modulus (MPa) MD 2,900 2,900 ASTM D 882
TD 2,900 2,900
Tensile strength (MPa) MD 220 220
TD 220 220
Tensile elongation (%) MD 110 110
TD 110 110
Tear strength (N/cm) MD 60 60 JIS Z 1702
TD 60 60
Impact strength (J/m) 59,000 59,000 Idemitsu method (1/2 inch head 2.9N-m)
Anti-pinhole strength (N)*1 10.0 10.0 JAS Idemitsu method (1 mm φ)
Static friction coefficient (tanθ) Int./int. 0.60 0.60 Idemitsu method (gradient method)
Out./out. 0.35 0.60
Haze (%) 4.0 4.0 ASTM D 1003
Gloss (%) 140 140 ASTM D 523
O2 transmission (cc/m2-24h) 15 15 Idemitsu method (mocon) 60%Rh
Water vapor transmission (g/m2-24h) 170 170 Infrared method
Water vapor shrinkage (%)
95°C x 30 min.		 MD 4.0 4.0 Idemitsu method
TD 2.5 2.5
Water vapor shrinkage (%)
120°C x 30 min.		 MD 7.0 7.0
TD 5.5 5.5
Corona processed surface Inner surface Both surfaces  
Winding length (m) 4,000 m roll/2,000 m roll  
*1
Anti-pinhole strength: pin diameter = 1.0 mm φ, speed 200 mm/min.
*
Data described in this document is a representative example of measured values under specific conditions.
*
Contents of this document are subject to change without prior notice due to product improvement.