| Category | Bi-axially oriented nylon film | ||
| Grade name | UNILON S-330 | Test method | |
| Application | Cover material for container | ||
| Characteristics | Balanced hot water shrinkage property | ||
| Thickness (µm) | 15 | - | |
| Tensile modulus (MPa) | MD | 2,200 | ASTM D 882 |
| TD | 2,100 | ||
| Tensile strength (MPa) | MD | 300 | |
| TD | 320 | ||
| Tensile elongation (%) | MD | 130 | |
| TD | 120 | ||
| Tear strength (N/cm) | MD | 80 | JIS J 1702 |
| TD | 80 | ||
| Impact strength (J/m) | 101,000 | Idemitsu method (1/2 inch head 2.9N-m) | |
| Anti-pinhole strength (N)*1 | 7.0 | JAS Idemitsu method (1 mm φ) | |
| Static friction coefficient (tanθ) | Int./int. | 1.00 | Idemitsu method (gradient method) |
| Out./out. | 0.50 | ||
| Haze (%) | 2.0 | ASTM D 1003 | |
| Gloss (%) | 140 | ASTM D 523 | |
| O2 transmission (cc/m2-24h) | 61 | Idemitsu method (mocon) | |
| 60%Rh | |||
| Water vapor transmission (g/m2-24h) | 240 | Infrared method | |
| Water vapor shrinkage (%) 95°C x 30 min. |
MD | 4.8 | Idemitsu method |
| TD | 4.8 | ||
| Water vapor shrinkage (%) 120°C x 30 min. |
MD | - | |
| TD | - | ||
| Standard thickness (µm) | 15 | ||
| Corona processed surface | Inner surface | ||
| Winding length (m) | 4,000 m roll/2,000 m roll | ||